Stick electrode 1.4370 (307 B), size: 5.0 mm Ø, 450 mm long, 130 - 160 A, PU = 65 pieces / 6.0 kg ~ MTC 1.4370 (307 B) ~ 307 B (Electr.) ~ 781MTC0004 ~ Schweiss Shop

307 B (Electr.) · 781MTC0004

coated electrode, size: 5,0 mm Ø, 450 mm long, 130 - 160 A, content = 65 pcs / 6,0 kg, DIN 8556: E 18 8 Mn B 20+, material number: corresponds 1.4370, AWS/ASME SFA-5.4: similar E 307 - 15, NF A 81 - 343: EZ 18.8 Mn B 20, EN 1600: E 18 8 Mn B 22.

Fig. may deviate

Description

Basic coated Rod electrodes for joint welding of different types of steel and for weld cladding. Weld metal made of austenitic chromium-nickel-manganese steel for operating temperatures up to +300°C, cold-tough up to -120°C.

DIN 8556: E 18 8 Mn B 20+, material no.: corresponds to 1.4370, AWS/ASME SFA-5.4: similar to E 307 - 15, NF A 81 - 343: EZ 18.8 Mn B 20, EN 1600: E 18 8 Mn B 22.

Most important base materials
Various types of steel (black/white compounds); high carbon and difficult to weld steel, manganese hard steel e.g. X 120 Mn 12 (1.3401); buffer layers for hardfacing, cold toughness steel, e.g. 10 Ni 14 (1.5637), 12 Ni 19 (1.5680)

Directional analysis of the pure weld metal in %
C Si Mn Cr Ni
0,10 0,5 6,5 18 8

Microstructure
Austenite, small amounts of delta ferrite possible

Special notes
Suitable for welding steel with higher phosphorus and sulphur content. Highest operating temperature for black/white joints +300°C. For prolonged annealing above +300°C or for operating temperatures above +300°C, nickel-based filler metals should be used. When welding cold-tempered nickel steel, observe the DVS 1501 information sheet. Scale resistant. Up to + 850°C.

Re-drying
Generally not necessary. However, the casing can withstand re-drying up to +350°C.