coated electrode, size: 4,0 mm Ø, 450 mm long, 140 - 185 A, content = 85 pcs / 6,0 kg, DIN 8529: EY 4243 MN B; AWS/ASME SFA-5.5: E 8018-G.
Fig. may deviate
Description
Basic coated Rod electrodes for welding high-strength and difficult-to-weld steels. Weld metal made of manganese-containing steel for operating temperatures from -10°C - +450°C. | ||||||
| DIN 8529: EY 4243 MN B; AWS/ASME SFA-5.5: E 8018-G.DIN 8529: EY 4243 MN B; AWS/ASME SFA-5.5: E 8018-G. | ||||||
|---|---|---|---|---|---|---|
| Directional analysis of the pure weld metal in % | ||||||
| ||||||
| Range of application The weld metal is extremely insensitive to cold and hot cracking, therefore particularly suitable for welding steels with high C-content (up to approx. 0.60% C). High notch impact values at low temperatures. 120% yield. Well suited for joint welding of rail steels. Easy weldability in all positions, low spatter losses, well covering, easily removable slag. | ||||||
| Re-drying Type of current/polarity Important base materials St 50, St 60, St 70; St 55, St 55.4; GS-52, GS-60; H III, H IV; 17 Mn 4, 19 Mn 5; rail steels; C 25, C 35, C 45 |