Stick electrode, size: 3.25 mm Ø, 350 mm long, welding current: 120 - 140 A, PU = 112 pieces / 3.9 kg ~ MTC CrMo 1 (3,25x350) ~ CrMo 1 (Electr.) WN.1.7339 ~ 769MTC0002 ~ Schweiss Shop

Start▸ Products▸ Filler materials▸ Stick electrodes▸ MTC▸ Structural steels / medium-leg.▸ CrMo 1 (Electr.) WN.1.7339

CrMo 1 (Electr.) WN.1.7339 · 769MTC0002

Name: Stick electrode, size: 3.25 mm Ø, 350 mm long, welding current: 120 - 140 A, PU = 112 pieces / 3.9 kg
Brand: MTC
SKU: 769MTC0002
Price: 46.36 EUR
Availability: InStock

Stick electrode WN.1.7339, MT-CrMo1 Size: 3.25 mm Ø, 350 mm long, welding current: 120 - 140 A, PU = 105 pieces / 3.9 kg

Fig. may deviate

Description

Basic coated stick electrode for welding creep resistant andhydrogen pressure resistantsteels.
Weld metal made of chromium- molybdenum-containingsteelforoperating temperaturesup to+550°C.

DIN 8575: E CrMo 1 B 20+, AWS/ASME SFA-5.5: E 8018 - B 2, B.S. 2493: E 1 CrMo B 26, NF A 81 - 345: E 1 CrMo B 26 2 H, EN 1599: E CrMo 1 B 42.

Most important base materials
1.7335, 13 CrMo 4 4, 1.7350, 22 CrMo 4 4, 1.7357, GS-17CrMo55, 1.7354, GS - 22 CrMo 5 4,
1.7337, 16 CrMo 4 4, 1.7225, 42 CrMo 4, 1.7218, 25CrMo4, 1.0407, LSt 45.8, 1.7218, GS -25 CrMo 4, 1.0569, LStE 36

Directional analysis of the pure weld metal in %

C	Si	Mn	Cr	Mo
0,07	0,3	1	1,1	0,5

Special notes
Preheat temperature +200 to +350°C; interpass temperature max. 350°C;
Heat treatment after welding: at least 1/2 h at 660 - 700°C,
Cooling in still air. After tempering, the weld metal is resistant to intergranular stress corrosion cracking (caustic cracks).

Re-drying
1 h at 300°C

Welding positions according to DIN EN ISO 6947
PA, PB, PC, PD, PE, PF

Current type/polarity
= +

Questions about the product?

Seen cheaper?

Share…

Back

Directly into the shopping cart

Manufacturer	MTC
Manufacturer number	CrMo 1 (3,25x350)
Product group	CrMo 1 (Electr.) WN.1.7339
Weight	3.90 kg
Content	3 Kilogram
Customs tariff number	83111000
Available	From stock (4-7 days after order)
Updated	02.09.2024

Stick electrode, size: 3.25 mm Ø, 350 mm long, welding current: 120 - 140 A, PU = 112 pieces / 3.9 kg ~ MTC CrMo 1 (3,25x350) ~ CrMo 1 (Electr.) WN.1.7339 ~ 769MTC0002 ~ Schweiss Shop

CrMo 1 (Electr.) WN.1.7339 · 769MTC0002

Stick electrode WN.1.7339, MT-CrMo1 Size: 3.25 mm Ø, 350 mm long, welding current: 120 - 140 A, PU = 105 pieces / 3.9 kg

Basic coated stick electrode for welding creep resistant andhydrogen pressure resistantsteels. Weld metal made of chromium- molybdenum-containingsteelforoperating temperaturesup to+550°C.

Most important base materials 1.7335, 13 CrMo 4 4, 1.7350, 22 CrMo 4 4, 1.7357, GS-17CrMo55, 1.7354, GS - 22 CrMo 5 4, 1.7337, 16 CrMo 4 4, 1.7225, 42 CrMo 4, 1.7218, 25CrMo4, 1.0407, LSt 45.8, 1.7218, GS -25 CrMo 4, 1.0569, LStE 36

Special notes Preheat temperature +200 to +350°C; interpass temperature max. 350°C; Heat treatment after welding: at least 1/2 h at 660 - 700°C, Cooling in still air. After tempering, the weld metal is resistant to intergranular stress corrosion cracking (caustic cracks).

Basic coated stick electrode for welding creep resistant andhydrogen pressure resistantsteels.
Weld metal made of chromium- molybdenum-containingsteelforoperating temperaturesup to+550°C.

Most important base materials
1.7335, 13 CrMo 4 4, 1.7350, 22 CrMo 4 4, 1.7357, GS-17CrMo55, 1.7354, GS - 22 CrMo 5 4,
1.7337, 16 CrMo 4 4, 1.7225, 42 CrMo 4, 1.7218, 25CrMo4, 1.0407, LSt 45.8, 1.7218, GS -25 CrMo 4, 1.0569, LStE 36

Special notes
Preheat temperature +200 to +350°C; interpass temperature max. 350°C;
Heat treatment after welding: at least 1/2 h at 660 - 700°C,
Cooling in still air. After tempering, the weld metal is resistant to intergranular stress corrosion cracking (caustic cracks).