Stick electrode, size: 3.2 mm Ø, 350 mm long, welding current: 100 - 130 A, PU = 115 pieces / 4 kg ~ MTC NiMoCr90 (3,25x350) ~ NiMoCr 90 (Electr.) ~ 770MTC0002 ~ Schweiss Shop

NiMoCr 90 (Electr.) · 770MTC0002

Stick electrode, size: 3.2 mm Ø, 350 mm long, welding current: 100 - 130 A, PU = 115 pieces / 4 kg, DIN 8529: EY 69 75 Mn2NiCrMo B, AWSIASME SFA-5.5: E11018-G, NF A 81 - 340: EY 69 2Mn2NiCrMo B 110 20 BH, EN 757: E 69 2 Mn 2 NiCrMo B 42.

Fig. may deviate

Description

Basic coated stick electrode for welding high-strength quenched and tempered fine-grained structural steels. Water-controlled weld metal made of nickel-manganese-chromium containing steel for operating temperatures from -60°C - +450°C.

Most important base materials
StE 500 to StE 690 V;
WStE 500 to WStE 690;
TStE 500 to TStE 690;
1.6341 - 11 NiMoV 5 3 @.B. Welmonil43);
1.6343 and 1.8809 - 12 MnNiMo 5 5 (e.g. Welmonil 35);
1.6368 - 15 NiCuMoNb 5 (e.g. WB 36);
1.6780 - 15 NiCrMo 10 6 (e.g. HY 80);
1.6782 - 16 NiCrMo 12 6 (e.g. HY 100);
1.6919 - 11 NiMnCrMo 5 5 (e.g. FG 70 CTICV);
1.7279 - 17 MnCrMo 3 3 (e.g. N-A-XTRA 55 or 56 to N-A-XTRA 70);
1.8928 - StE 690 V (e.g. FG 70 V);

Directional analysis of the pure weld metal in %
C Si Mn Ni Cr Mo
0,05 0,3 1,7 2 0,4 0,4

Special instructions
Weld rod electrode at approx. 100°C intrinsic temperature. Preheat base material to 50 - 100°C depending on sheet thickness. Interpass temperature should not exceed 200°C. In order to influence the quenching and tempering properties of the base material as little as possible, avoid pendulum movement with the stick electrode and aim for an extraction length of at least 0.5 X length of the stick electrode. For other types of steel, e.g. 42 CrMo 4) Preheat according to the base material.

Re-drying
2 h at 300 - 350°C; maximum time 10 h